China Factory Suppliers of Hot Spray Polyurea for Waterproofing, Surface Protection, and Industrial Floors
Characteristics of the product
1. Ultra-fast curing; continuous spraying available on curved surfaces, vertical walls and top surfaces without sagging.
2. Excellent waterproof performance to fully isolate substrates from water erosion.
3. Outstanding physical & chemical properties, strong adhesion to various base materials.
4. High construction efficiency; designed thickness can be achieved in one single pass.
5. Integral, dense and seamless coating film.
6. Mechanized spraying construction with stable, controllable film quality.
7. Solvent-free & heavy-metal-free, eco-friendly formula.
8. 100% solid content, zero VOC emission.
9. Wide service temperature range: -45 ℃ ~ 150 ℃.
10. Continuous compact seamless film, practical and attractive appearance.
Product Parameters
| No. | Test Item | Technical Requirement | Test Result |
|---|---|---|---|
| 1 | Solid Content (%) | ≥98 | 99 |
| 2 | Gel Time (s) | ≤45 | 16 |
| 3 | Surface Dry Time (s) | ≤120 | 20 |
| 4 | Tensile Strength (MPa) | ≥16.0 | 16.24 |
| 5 | Elongation at Break (%) | ≥450 | 460 |
| 6 | Tear Strength (N/mm) | ≥50 | 66 |
| 7 | Low-temperature Bending (℃) | ≤-40 | -40 |
| 8 | Water Impermeability | 0.4 MPa, impermeable for 2h | Impermeable |
| 9 | Heating Elongation (%) | Elongation / contraction ≤1.0 | 0.4 |
| 10 | Bond Strength (MPa) | ≥2.5 | 3 |
| 11 | Water Absorption (%) | ≤5.0 | 0.5 |
| 12 | Thermal Aging & Artificial Weathering Appearance | No cracks & deformation | No cracks & deformation |
| 13 | Thermal Aging Performance | ||
| Tensile Strength Retention Rate (%) | 80–150 | 97 | |
| Elongation at Break (%) | ≥400 | 411 | |
| Low-temperature Bending (℃) | ≤-35 | -35, no crack | |
| 14 | Alkali Resistance Performance | ||
| Tensile Strength Retention Rate (%) | 80–150 | 103 | |
| Elongation at Break (%) | ≥400 | 413 | |
| Low-temperature Bending (℃) | ≤-35 | -35, no crack | |
| 15 | Acid Resistance Performance | ||
| Tensile Strength Retention Rate (%) | 80–150 | 99 | |
| Elongation at Break (%) | ≥400 | 410 | |
| Low-temperature Bending (℃) | ≤-35 | -35, no crack | |
| 16 | Salt Resistance Performance | ||
| Tensile Strength Retention Rate (%) | 80–150 | 97 | |
| Elongation at Break (%) | ≥400 | 409 | |
| Low-temperature Bending (℃) | ≤-35 | -35, no crack | |
| 17 | Artificial Weathering Performance | ||
| Tensile Strength Retention Rate (%) | 80–150 | 83 | |
| Elongation at Break (%) | ≥400 | 408 | |
| Low-temperature Bending (℃) | ≤-35 | -35, no crack | |
| 18 | Hardness (Shore A) | ≥80 | 85 |
| 19 | Abrasion Loss (750g/500r, mg) | ≤30 | 1 |
| 20 | Impact Resistance (kg·m) | ≥1.0 | 1.0 kg·m, intact |
Application Scope & Construction Method
1. Chemical, petroleum & petrochemical industry: workshop floors, storage tanks, neutralization tanks, drainage trenches.
2. Environmental facilities: landfill sites, sewage treatment tanks, waste gas filtration towers.
3. Factory & warehouse floors: anti-corrosion and wear-resistant protection.
4. Steel structures: metal pipelines, bridge decks, ship decks and platforms.
5. Building waterproofing: roof waterproofing, exterior wall waterproofing & renovation.
6. Municipal facilities: sports grandstands, anti-seepage wear-resistant flooring.
7. Aquatic venues: water parks, swimming pools, aquaculture ponds.
Packaging specification
● Component A: 220 kg per drum
● Component B: 210 kg per drum
Storage
1. Store in sealed, cool, dry and ventilated warehouse; avoid direct sunlight, rain and all ignition sources.
2. Shelf life: 6 months under original sealed packaging and specified storage conditions.
3. Expired material can be reused only if re-inspection meets all technical indexes.
4. Use up quickly once opened; re-seal tightly for storage if unused.
5. Solvent-free product, classified as non-hazardous goods for transportation.
6. Strictly prevent rain, sunlight and violent collision during transit; stack materials neatly and stably, complying with transport regulations.
Construction Conditions
1. Substrate Requirements
Concrete base shall be cleaned, leveled and polished to form proper roughness. Concrete curing must be fully completed with strength ≥ C25 and moisture content ＜8%. Proceed to next process immediately after substrate treatment.
2. Ambient Temperature & Humidity
● Construction temperature: 5 ~ 35 ℃
● Substrate surface temperature shall be at least 5 ℃ higher than dew point
● Relative humidity: 30% ~ 80%
● Keep ventilation; stop construction under strong wind.
Coating Method & Requirements
1. Stir Component B thoroughly before use; volume mixing ratio A:B = 1:1.
2. Professional spraying equipment is mandatory; material temperature controlled at 50 ~ 80 ℃ during spraying.
3. Next process can be carried out after 12 hours curing. If interval exceeds 24 hours, apply interface agent before re-spraying.
4. If rain occurs after coating, apply interface agent before subsequent construction.
5. Full film curing time: minimum 7 days to achieve optimal comprehensive performance.
Recommended Consumption
Standard dosage: 1.2 kg per square meter per mm thickness
National standard waterproof thickness 1.5 mm: 1.8 kg/㎡
National standard anti-corrosion thickness 2.0 mm: 2.4 kg/㎡
Safety & Labor Protection
Read product manual and warning labels fully before operation; master construction specifications.
No open flame, welding or smoking on construction site; maintain good ventilation.
Although solvent-free, spray mist will be generated during spraying. Wear gas mask and full protective gear to avoid inhalation and direct skin contact.
Flush splashed coating on skin with detergent, soap and plenty of clean water immediately. For eye splashes, rinse thoroughly with water and seek medical treatment promptly.
Fully cured dry film is non-toxic under normal application conditions. For more details, please contact Shandong Century Union New Materials Technology Co., Ltd.
Construction steps
First step: clean the foundation, fill in the gaps
Second Step: Roll primer
Third step: self-leveling cold polyurea floor construction
Forth step: Brush waterbased PU top coat
Frequently Asked Questions (FAQ)
What substrates can this coating material be applied to?
This product demonstrates strong adhesion to various substrates including concrete floors, steel structures, metal pipelines, bridge and ship decks, storage tanks, and municipal structures.
How fast does the coating gel and become surface dry?
The product features ultra-fast curing, with a typical gel time of 16 seconds (≤45s) and a surface dry time of approximately 20 seconds (≤120s), allowing rapid application on vertical and overhead surfaces without sagging.
What are the required environmental and substrate conditions for application?
The concrete substrate must be fully cured (strength ≥ C25, moisture content < 8%). Construction temperature should range between 5 ℃ and 35 ℃, relative humidity between 30% and 80%, and substrate surface temperature at least 5 ℃ above the dew point.
What is the recommended material consumption for waterproofing versus anti-corrosion?
Standard consumption is 1.2 kg/㎡ per 1 mm thickness. For national standard waterproofing (1.5 mm thickness), recommended consumption is 1.8 kg/㎡; for anti-corrosion applications (2.0 mm thickness), recommended dosage is 2.4 kg/㎡.
What should be done if the interval between coating layers exceeds 24 hours?
If the recoat interval exceeds 24 hours or if the coating is exposed to rain, an interface agent must be applied to ensure optimal adhesion before subsequent coating layers.
Is the coating environmentally friendly and safe for transport?
Yes, it features a 100% solid content formula that is solvent-free, heavy-metal-free, and has zero VOC emissions. It is classified as non-hazardous goods for transportation.